产品名称：质子交换膜602*1102mm 型号:TR188-N-212库号：M56022
产品型号：N-212
所属类别：实验室仪器设备 > 其他实验仪器装置
发布时间：2023-12-13
已获点击：26

详细说明

N-212（50μm） 602*1102mm

产品规格型号N-212 厚度51(μm) 克重102.0(g/m2)

性能指extClass' contenteditable='false' tabind='-1'>标 Performance Ind

N-3010 N-3015 N-211/212

物理性能

Physical Properti

技术指extClass' contenteditable='false' tabind='-1'>标

Technical Ind

测试方法

Tt Method

拉伸测试 Tensile Tt

(23°C, 50% RH)

纵向

MD

横向

TD

纵向

MD

横向

TD

/

拉伸强度 Tensile

trength(MPa)

45 38 40 35 30 AextClass' contenteditable='false' tabind='-1'>TM D 882

弹性模量 Tensile

Modulu(MPa)

480 400 400 350 400 AextClass' contenteditable='false' tabind='-1'>TM D 882

断裂伸长率

Elongation at

break(%)

175 150 190 170 150/180 AextClass' contenteditable='false' tabind='-1'>TM D 882

比重 pecific Gravity 1.97 1.97 1.98 —

其它性能

Other properti

技术指extClass' contenteditable='false' tabind='-1'>标

Technical Ind

测试方法

Tt Method

电导率 2

Conductivity(/cm)

0.095 0.134 0.100

GB/T

20042.3-2009

透过率

3Hydrogen

Crossover(ml/min·cm

2)

＜0.010 ＜0.010 ＜0.015/0.010

GB/T

20042.3-2009

透氢电流密度 4

Hydrogen Crossover

Current(mA/cm2)

＜2.0 ＜2.0 / 科润 THINKE

水解性能

Hydrolytic Properti

技术指extClass' contenteditable='false' tabind='-1'>标

Ind Parameters

测试方法

Tt Method

含水量 5

Water Content(%)

10.0±3.0 10.0±3.0 5.0±3.0 AextClass' contenteditable='false' tabind='-1'>TM D570

WWW.THINKRE.CN

吸水率 6

Water Uptake(%)

50.0±5.0 50.0±5.0 50.0±5.0 AextClass' contenteditable='false' tabind='-1'>TM D570

厚度溶胀率

Thickns Change

从23°C, 50% RH到 23°C 浸泡

from 50% RH, 23°C to water soaked,23°C

10 15 10

AextClass' contenteditable='false' tabind='-1'>TM D756

厚度溶胀率

Thickns Change

从 23°C, 50% RH 到 100°C 浸

泡

from 50% RH, 23°C to water soaked,100°C

30 40 30 AextClass' contenteditable='false' tabind='-1'>TM D756

纵向

MD

横向

TD

纵向

MD

横向

TD

/

线性溶胀率

Linear pansion

从23°C, 50% RH到 23°C 浸泡

from 50% RH, 23°C to water soaked,23°C

3 4 3 5 4 AextClass' contenteditable='false' tabind='-1'>TM D756

线性溶胀率

Linear pansion

从23°C, 50% RH到 23°C 浸泡

from 50% RH, 23°C to water soaked,100°C

5 2 10 5 20 AextClass' contenteditable='false' tabind='-1'>TM D756

1膜测试前在 23°C, 50% RH 环境extClass' contenteditable='false' tabind='-1'>下至少放置 24h。

Measurements taken with membrane conditioned to 23°C, 50% RH. 2电导率测试是 23°C, RH extClass' contenteditable='false' tabind='-1'>下进行。

Conductivity measurements a 23 °C, RH. 3透过率测试是在 23°C, RH extClass' contenteditable='false' tabind='-1'>下进行的。

Hydrogen crossover measured at 23 °C, RH. 4透氢电流测试：将膜组装做成 MEA，在 80°C 完水和状态extClass' contenteditable='false' tabind='-1'>下进行的。

Hydrogen crossover Current measured in MEA on H2, 80°C, fully humidified gas. 5膜在 23°C, 50% RH 环境extClass' contenteditable='false' tabind='-1'>下相对于干膜的含水量。

Water content of membrane conditioned to 23 °C and 50% RH (dry weight basis). 6膜在 100°C, 水煮 1h 后相对于干膜的吸水率。

Water uptake from dry membrane to conditioned in water at 100 °C for 1 hour (dry weight basis).

WWW.THINKRE.CN

NEPEM-11 系列膜产品说明

重量 1KG内